Anode material for lithium-ion chemical power sources and method of obtaining thereof

ABSTRACT

Field of use: the electrotechnical industry, in particular, anode materials for lithium-ion ECCs. Essence of the invention: Anode material based on lithium-titanium spinel that contains doping components, chromium and vanadium, in equivalent quantities, of the chemical formula Li4Ti5-2y(CryVy)O12-x, where x is the deviation from stoichiometry within the limits 0.02&lt;x&lt;0.5, and y is the stoichiometric coefficient within the limits 0&lt;y&lt;0.1.

RELATED APPLICATIONS

This application claims priority to Russian Patent Application No. RU2009107944 filed on Mar. 6, 2009, which is incorporated herein by reference in its entirety.

FIELD OF THE INVENTION

The invention relates to electrotechnical industry, in particular, to anode materials for ECCs (electrochemical cells), and can be used as the starting material for lithium-ion secondary batteries (storage batteries) designed for applications requiring large capacitance and high operating currents, for example, electric transport—HEV (hybrid electric vehicles), PHEV (plug-in hybrid electric vehicles), BEV (battery electric vehicles), or portable electric power tools.

BACKGROUND OF THE INVENTION

The most widely used couple in lithium-ion storage batteries is the LiCoO₂/C (carbon) couple. However, the compound LiC₆ that is formed when lithium ions are inserted into a carbon structure, for example, graphite, is explosion hazardous. The drawbacks of graphite include alteration of the structure during operation and an initial loss of capacitance up to 20%. These drawbacks lead to the necessity of using other materials as the anode, for example, lithium-titanium spinel, Li₄Ti₅O₁₂ (in alternate notation, Li_(4/3)Ti_(5/3)O₄).

[J. Li, Y-L. Jin, X.-G. Zhang, H. Yang. Microwave solid-state synthesis of spinel Li₄Ti₅O₁₂ nanocrystallites as anode material for lithium-ion batteries//Solid State Ionics.—2007,—V. 178.—P. 1590-1594.; Xu J., Wang Y., Li Z., Zhang W. F. Preparation and electrochemical properties of carbon-doped TiO₂ nanotubes as an anode material for lithium-ion batteries//Journal of Power Sources.—2008,—V. 175.—P. 903-908; Li₄Ti₅O₁₂ as anode in all-solid-state, plastic, lithium-ion batteries for low-power applications//P. P. Prosini, R. Mancini, L. Petrucci et al.//Solid State Ionics.—2001, V.—144.—P. 185-192.]

Anode materials for lithium-ion electrochemical cells, lithium-titanium spinels, in particular Li₄Ti₅O₁₂, began to be regarded as promising material for lithium batteries since the mid-1980s.

[D. W. Murphy, R. J. Cava, S. Zahurak, A. Santoro. Ternary Li_(x)TiO₂ phases from insertion reactions//Solid State Ionics.—1983.—V. 9-10.—P. 413-417; K. M. Colbow, J. R. Dahn and R. R. Haering. Structure and Electrochemistry of Spinel Oxides LiTi₂O₄ and Li_(4/3)Ti_(5/3)O₄//J. of Power Sources.—1989.—V. 26,—N. 3/4.—P. 397-402; T. Ohzuku, A. Ueda, N. Yamamoto. Zero-Strain Insertion Material of Li[Li_(1/3)Ti_(5/3)]O₄ for Rechargeable Lithium Cells//J. Electrochem. Soc.—1995.—V. 142.—I. 5.—P. 1431-1435].

One formula unit of this substance is capable of accepting three lithium ions. The electrochemical discharge process is described by the following reaction: Li₄Ti₅O₁₂+3e⁻+3Li⁺=Li₇Ti₅O₁₂

The theoretical specific capacitance of the substance in the process described by the equation is 175 mA-h/g. As a result of this reaction, the initial structure of the substance of the spinel type shifts to a metastable phase with an ordered structure of the NaCl type. As distinct from the majority of the known electrode materials for lithium-ion ECCs, the electromotive force of which depends on the degree of discharge of the material (expressed as the subscript x of lithium in the formula of the active substance, for example, Li_(x)CoO₂), in this case it is determined by the twophase equilibrium, (Li₄Ti₅O₁₂)^(spinel)/(Li₇Ti₅O¹²)^(quasi-NaCl), and therefore is constant and is E^(o)=1.55 V in relation to metallic lithium.

The crystallographic notation of this concentration transition for the tripled formula unit of the classical spinel (3×AB₂O₄=A₃B₆O₁₂, where A and B are atoms at the tetrahedral and octahedral sites of the structure, respectively) has the following appearance: Li^(A) ₃(LiTi₅)^(B)O₁₂+3Li→Li₆(LiTi₅)O₁₂≡B′₆B₆O₁₂

This formula expresses the formation of two non-equivalent sublattices with octahedral sites of the 16c and 16d type. Since the initial tetrahedral sites in the process described become octahedral through filling with additional lithium atoms (8a→16c), this concentration phase transition is possible only if all tetrahedral sites in the initial spinel structure are occupied by mobile lithium. If an atom not capable of transition to 16c octahedral sites in the course of the process under discussion is present at 8a tetrahedral sites, the process is “frozen,” and a reversible charge-discharge electrochemical reaction, as occurs, for example, in the case of doping of a lithium-titanium spinel with iron, is impossible.

[P. Kubiak, A. Garcia, M. Womes, L. Aldon, J. Olivier-Fourcade, P.-E. Lippens, J.-C. Jumas. Phase transition in the spinel Li₄Ti₅O₁₂ induced by lithium insertion. Influence of the substitutions Ti/V, Ti/Mn, Ti/Fe. //J. Power Sources.—2003.—V. 119-121.—P. 626-630].

As the electromotive force of the potential-generating reaction in relation to metallic lithium, E⁰ _(Li), is equal to 1.55 V, thus with the use of this substance as an anode, the electromotive force of the cell is substantially lower than with the use of the traditional carbon electrode (C₆—LiC₆; E⁰ _(Li)≈0.1 V), and resulting specific energy of the material is not large, but this drawback is redeemed by the unique cycleability of the material. Since the volume changes are negligible, 0.07%, in the case of the Li₄Ti₅O₁₂→Li₇Ti₅O₁₂ transition, this is regarded as a highly favorable factor fostering cycle life, as the mechanical degradation of the macrostructure of the electrode is excluded. The low cost of the initial raw material, compounds of titanium, is also of considerable significance for marketing prospects of the material. In addition, the charged form of the material, Li₇Ti₅O₁₂, is entirely safe, unlike LiC₆, and all the more so, metallic lithium, which are spontaneously inflammable in air (for example, when the electric cell is destroyed).

[E. Ferg, R. J. Gummow, A. de Kock, M. M. Thackeray. Spinel Anodes for Lithium-Ion Batteries//J. Electrochem. Soc.—1994.—V. 141.—I. 11.—P. L147-L150; K. Zaghib, M. Armand, M. Gauthier. Electrochemistry of Anodes in Solid-State Li-Ion Polymer Batteries//J. Electrochem. Soc.—1998.—M. 145.—I. 9.—P. 3135-3140; A. D. Robertson, L. Trevino, H. Tukamoto, J. T. S. Irvine. New inorganic spinel oxides for use as negative electrode materials in future lithium-ion batteries//J. of Power Sources.—1999.—V. 81-82.—P. 352-357; see also RF patent No. 2304325, published Aug. 10, 2007].

The aggregate of these properties makes it possible to regard the lithium-titanium spinel as a highly promising anode material for lithium electric cells. However, the low electron conduction of the material and, as a result, the low degree of operating capacitance extraction (not more than 160 mA-h/g, e.g., not more than 90% of the theoretical), especially at high current densities, is the main impediment to the use of this material in the mass production of electric cells.

The reason for the low electron conduction is the absence of charge carriers in the structure of this substance, making it virtually a dielectric. The titanium in this structure has the highest oxidation state, 4+, and the charge balance can be expressed by the formula Li⁺ ₄Ti⁴⁺ ₅O²⁻ ₁₂. Since the titanium 4+ ion has a 3d⁰ electronic configuration, the valence band is completely filled and the conduction band is completely empty. The electron conduction, therefore, as for other dielectrics, is determined by the “prehistory” of the specimen, in the first place by the presence and concentration of impurities that produce donor and acceptor levels, as well as by its intrinsic imperfection. According to the data of many published sources, the electron conduction of Li₄Ti₅O₁₂ under normal conditions lies in the interval, 10⁻⁸-10⁻¹³ ohm⁻¹·cm⁻¹.

[C. H. Chen, J. T. Vaughey, A. N. Jansen, D. W. Dees, A. J. Kahaian, T. Goacher, M. M. Thackeray. Studies of Mg-Substituted Li_(4-x)Mg_(x)Ti₅O₁₂ Spinel Electrodes (0<x<1) for Lithium Batteries//J. Electrochem. Soc.,—2001,—V. 148,—P. A102.; I. A. Leonidov, O. N. Leonidova, O. F. Samigullina, M. V. Patrakeev. Structural Aspects of Lithium Transfer in Solid Electrolytes Li2xZn2-3xTi1+xO4 (0.33≦x≦0.67)//Zhurnal strukturnoy khimii [Journal of Structural Chemistry].—2004.—V. 45.—No. 2.—P. 262-268; M. Wilkening, R. Amade, W. Iwaniak, P. Heitjans. Ultraslow Li diffusion in spinel-type structured Li₄Ti₅O₁₂—A comparison of results from solid state NMR and impedance spectroscopy//Phys. Chem. Chem. Phys.—2007—V. 9—P. 1239-1246; see also U.S. Pat. No. 7,211,350, date of issue May 1, 2007; U.S. Pat. No. 6,379,843, date of issue Apr. 30, 2002 (Europatent EP 0 845 825 B1, issued Jan. 21, 2004); US applications US20070238023, published Oct. 11, 2007; US 20070243467, published Oct. 18, 2007;].

Several methods are known for increasing the electron conduction of a lithium-titanium spinel. The creation of a twophase composition comprising an electrochemically active substance, in this case Li₄Ti₅O₁₂, and an electroconductive additive that is uniformly distributed among the lithium titanate particles, is possible. Both mechanical mixtures of the electrode material and various forms of carbon, as well as chemically deposited films of carbon on lithium titanate, are used. The development of this logic has led to the creation of a material with a carbon electroconductive coating on Li₄Ti₅O₁₂ particles.

[L. Cheng, X. Li, H. Liu, H. Xiong, P. Zhang, Y. Xia. Carbon-Coated Li₄Ti₅O₁₂ as a High Rate Electrode Material for Li-Ion Intercalation//J. Electrochem. Soc.—2007.—V. 154.—I. 7.—P. A692-A697; R. Dominko, M. Gaberscek, M. Bele, D. Mihailovic, J. Jamnik. Carbon nanocoatings on active materials for Li-ion batteries.//J. of the Eur. Cer. Soc.—2007.—V. 27.—I. 2-3.—P. 909-913; US application US2008/0315161, published Dec. 25, 2008]

Metals, in particular copper and silver, as well as an intermetallide, titanium nitride (TiN), have also been proposed as such electroconductive additives. The current characteristics of the anode material are improved by means of the creation of disperse two-phase compositions, obtained in particular by in situ methods. The use of compositions with electroconductive polymers has also been proposed.

[S. Huang, Z. Wen, J. Zhang, X. Yang. Improving the electrochemical performance of Li₄Ti₅O₁₂/Ag composite by an electroless deposition method//Electrochimica Acta.—2007.—V. 52.—I. 11.—P. 3704-3708; S. Huang, Z. Wen, B. Lin, J. Han, X. Xu. The high-rate performance of the Newly Designed Li₄Ti₅O₁₂/Cu composite anode for lithium ion batteries//Journal of Alloys and Compounds.—2008.—V. 457,—I. 1-2.—P. 400-403; S. Huang, Z. Wen, J. Zhang, Z. Gu, Xi. Li₄Ti₅O₁₂/Ag composite as electrode materials for lithium-ion battery//Solid State Ionics.—2006. V. 177.—I. 9-10.—P. 851-855; M. Q. Snyder, S. A. Trebukhova, B. Ravdel, M. C. Wheeler, J. DiCarlo, C. P. Tripp, W. J. DeSisto. Synthesis and characterization of atomic layer deposited titanium nitride thin films on lithium titanate spinel powder as a lithium-ion battery anode//Journal of Power Sources—2007—V. 165.—P. 379-385; H. Yu, H. Xie, A. F. Jalbout, X. Yan, X. Pan, R. Wang, High-rate characteristics of novel anode Li₄Ti₅O₁₂/polyacene materials for Li-ion secondary batteries//Electrochimica Acta.—2007.—V. 53.—I. 12,—P. 4200-4204.]

While increasing the total electroconductivity of the composition, these methods do little to improve the local conditions of discharge of the particles of the electrode material beyond the limits of the direct electrode material-electroconductive additive contact. In addition, conductive surface additives operate only at the initial stage of the electrochemical intercalation of lithium into the material. It should be taken into consideration that the Li₇Ti₅O₁₂phase obtained from the initial material upon its discharge is a very good conductor, since it contains a high concentration of Ti³⁺ (3d¹), i.e., electrons in the conduction band (in accordance with the formula Li₇Ti³⁺ ₃Ti⁴⁺ ₂O₁₂). Therefore, the Li₄Ti₅O₁₂ particles (starting from the composition Li_(4+δ)Ti₅O₁₂, where δ≈0.1, i.e.˜ 1/30 of the total capacitance) are already coated with a current-conducting layer of Li₇Ti₅O₁₂ at the initial stages of the process, which makes the presence of a preliminarily created layer superfluous. Subsequently the process takes place along the interphase boundary between Li₄Ti₅O₁ and Li₇Ti₅O₁₂, i.e., the lithium ions and electrons enter the reaction zone through the Li₇Ti₅O₁₂ layer. The reverse process (discharge) must proceed in an entirely different manner, since a non-conductive layer of Li₄Ti₅O₁₂ is formed in its turn at the surface of the Li₇Ti₅O₁₂particles (at least at high rates of discharge) and the lithium ions and electrons now enter the reaction zone through the Li₄Ti₅O₁₂ layer. In this case the presence of an electroconductive layer at the surface of the particles is not crucial for some significant improvement of the kinetics of the electrode process.

[S. Scharner, W. Wepner, P. Schmid-Beurmann. Evidence of Two-Phase Formation upon Lithium insertion into the Li_(1.33)Ti_(1.67)O₄ Spinel//J. Electrochem. Soc.—1999.—V. 146.—I. 5.—P. 857-861; W. Lu, I. Belharouak, J. Liu, K. Amine. Electrochemical and Thermal Investigation of Li_(4/3)Ti_(5/3)O₄ Spinel//J. of the Electrochemical Society,—2007.—V. 154.—P. A114-A118; F. Ronci, P. Reale, B. Scrosati, S. Panero, V. R. Albertini, P. Perfetti, M. di Michiel, J. M. Merino. High-Resolution In-Situ Structural Measurements of the Li_(4/3)Ti_(5/3)O₄ “Zero-Strain” Insertion Material.//J. Phys. Chem. B,—2002.—V. 106,—P. 3082].

A second approach to improving electron conduction is the introduction of impurities, or doping, i.e., the partial substitution of structure-forming ions by other ions, as a rule, in a different charge state. In the process the concentration of the doping element is such that the type of crystalline structure of the initial substance is unchanged. Impurity charge defects serving as carriers of electric current are formed in the substance as a result of such substitution. In case of the absence or extremely low concentration of its intrinsic current carriers, the occurrence of such extrinsic carriers may alter the conductivity of the substance by many orders of magnitude.

In the known methods of producing anode materials, substantial substitution of titanium by molybdenum with simultaneous reduction of molybdenum to the Mo⁴⁺ state results in improvement of the conductivity of the final product. Thus, the measured electrical conductivities for Li₄Ti_(4.5)Mo_(0.5)O₁₂, Li₄Ti₄MoO₁₂, and Li₄Ti_(3.5)Mo_(1.5)O₁₂ are 1.6, 2.8, and 5.8 10⁻³ ohm⁻¹·cm⁻¹, respectively. However, molybdenum is not a “good” doping element for the mass production of lithium-titanium spinel, as the cost of its reagents is high.

[Z. Zhong. Synthesis of Mo⁴⁺ Substituted Spinel Li₄Ti_(5-x)Mo_(x)O₁₂//Electrochemical and Solid-State Letters,—2007,—V. 10—N. 12—P. A267-A269; US application US2009/0004563, published Jan. 1, 2009].

In other known methods, the substitution of titanium in Li₄Ti₅O₁₂ by iron, nickel, vanadium, and manganese results in the appearance of these elements both at the octahedral and the tetrahedral sites of the structure. This depresses the concentration phase transition and degrades the electrochemical properties of the material. The results of electrochemical studies of these substituted compositions leads to the same conclusions. Attempts have been made at the substitution of titanium by other elements as well, for example, Al, Ga, and Co, or at substitution in an anion sublattice.

[S. Scharner, W. Wepner, P. Schmid-Beurmann. Evidence of Two-Phase Formation upon Lithium insertion into the Li_(1.33)Ti_(1.67)O₄ Spinel//J. Electrochem. Soc.—1999.—V. 146.—I. 5.—P. 857-861; A. D. Robertson, L. Trevino, H. Tukamoto, J. T. S. Irvine. New inorganic spinel oxides for use as negative electrode materials in future lithium-ion batteries//J. of Power Sources.—1999.—V. 81-82.—P. 352-357; A. D. Roberston [sic], H. Tukamoto, J. T. S. Irvine.//J. Electrochem. Soc. 146 (1999) P. 3958; P. Kubiak, A. Garcia, M. Womes, L. Aldon, J. Olivier-Fourcade, P.-E. Lippens, J.-C. Jumas. Phase transition in the spinel Li₄Ti₅O₁₂ induced by lithium insertion. Influence of the substitutions Ti/V, Ti/Mn, Ti/Fe.//J. Power Sources.—2003.—V. 119-121.—P. 626-630; S. Huang, Z. Wen, X. Zhu, Z. Lin. Effects of dopant on the electrochemical performance of Li₄Ti₅O₁₂ as electrode material for lithium ion batteries.//J. of Power Sources.—2007.—V. 165.—I. 1.—P. 408-412; S. Huang, Z. Wen, Z. Gu, X. Zhu. Preparation and cycling performance of Al³⁺ and F⁻ co-substituted compounds Li₄Al_(x)Ti_(5-x)F_(y)O_(12-y). //Electrochimica Acta—2005.—V. 50.—I. 20.—P. 4057-4062].

A new approach was demonstrated in a method according to which, by means of heat treatment of samples of lithium titanate at high temperatures in a reducing gaseous environment, materials of the composition, Li₄Ti₅O_(12-δ), where δ≦0.012, that are reduced in the anion sublattice, are obtained. Such nonstoichiometry with respect to oxygen leads to a sharp increase in electronic conductivity, approximately to 10⁻⁶-3·10⁻⁶ S/cm under normal conditions (temperature 298° K) due to the partial removal of oxygen with preservation of the crystalline structure. However, exceeding the limiting value δ=0.012 leads to loss of stability of the crystalline structure and decay of the spinel phase to compounds with structures of the Li₂Ti₃O₇ and γ-Li₂TiO₃ types.

[V. Gorchkov, O. Volkov. Lithium titanate and method of forming the same. U.S. Pat. No. 7,541,016, issued Jun. 2, 2009].

The traditional approach of intensification of the electrode process in active materials of ECCs—the production of an electrode with a high specific surface area and small effective particle size (for example, by the sol-gel or dry-spray [dry spraying] methods), does not lead to improvement of the discharge characteristics, since the resulting increase in the surface of the electrolyte and electrode contact does not decrease ohmic resistance, and the extremely low electronic conductivity of the electrode is a limiting factor. Decreasing the size of the particles leads to deterioration of cycleability at high discharge rates, especially at low temperatures.

[J. L. Allen, T. R. Jow, J. Wolfenstine. Low temperature performance of nanophase Li₄Ti₅O₁₂. J. of Power Sources.—2006.—V. 159.—I. 2. P. 1340-1345; U.S. Pat. No. 7,368,097, date of issue May 6, 2008; U.S. Pat. No. 6,881,393, date of issue Apr. 19, 2005].

All known anode materials based on lithium-titanium spinel for ECCs produced by the methods described above possess inadequate electronic conductivity, and as a consequence thereof, limited electrochemical capacitance and cycleability at high operating currents that impede use in devices with high wattage consumption. At the same time, the cost of the initial components is high and the production methods are complicated.

There is a known anode material for lithium-ion ECCs based on lithium-titanium spinel of the chemical formula, Li₄Ti₅O_(12-x), where x is the deviation from stoichiometry with respect to oxygen, within the limits of 0<x<0.02, that is closest to the invention being applied for in technical essence and result to be achieved.

The known method—the prototype of the production of said anode material for lithium-ion ECCs, includes preparation of a mixture of the initial components, that contain lithium and titanium, by means of homogenization and pulverization, with subsequent heat treatment of the prepared mixture in a controlled atmosphere of inert and reducing gases. Wherewith hydrogen, hydrocarbons, and carbon monoxide are used as reducing gases and the reduction process (heat treatment) is run at a temperature of 450° C. for 30 minutes.

[see US application No. US 2007/0238023, IPC H01M 4/48, C01G 23/04, published Oct. 11, 2007; patent issued to V. Gorshkov, O. Volkov. Lithium titanate and method of forming the same. U.S. Pat. No. 7,541,016 B2. Jun. 2, 2009].

The characteristics of the known anode material for lithium-ion ECCs produced by method described above are given in the Table.

Although the known material possesses high electrochemical capacitance, and good cycleability, it does not operate at high discharge currents due to low electronic conductivity.

SUMMARY OF THE INVENTION

The objective of the present invention is to produce anode material for lithium-ion ECCs that possesses high electronic conductivity and electrochemical capacitance for use in devices with operating at high discharge currents.

The stated objective is achieved by the fact that the known anode material for lithium-ion ECCs based on lithium-titanium spinel of the chemical formula, Li₄Ti₅O_(12-x),

where x is the deviation from stoichiometry within the limits 0<x<0.02,

ACCORDING TO THE INVENTION, contains doping components, chromium and vanadium, in equivalent quantities to achieve a composition of the formula, Li₄Ti_(5-2y)(Cr_(y)V_(y))O_(12-x),

where 0.02<x<0.5, and y is the stoichiometric coefficient within the limits 0<y<0.25.

In the known method of production of anode material for lithium-ion ECCs, which includes preparation of a mixture of the initial components, that contain lithium and titanium, by means of homogenization and pulverization, with subsequent heat treatment of the prepared mixture in controlled atmosphere of inert and reducing gases,

ACCORDING TO THE INVENTION, sources of doping elements, chromium and vanadium, are introduced into the mixture of initial components, the pulverization is carried out until particles no greater than 0.5 mcm in size are obtained, and the heat treatment is carried out stepwise in an atmosphere of argon and acetylene, regulating the volume ratio of the gases in the argon-acetylene stream from 999:1 to 750:250, respectively, according to the following procedure:

-   -   at the first stage the mixture of components is heated to a         temperature no higher than 350° C.;     -   at the second stage the heating is continued in the 350-750° C.         temperature interval at a rate no greater than 10° C./min, which         provides for solid-phase interaction of the components;     -   at the third stage the temperature is increased to 840-850° C.         and the product obtained is held at this temperature no less         than 1 hour;     -   at the fourth stage the temperature is decreased to 520-580° C.         at a rate no greater than 5° C./min, and the anode material         obtained is held at this temperature no less than 2 hours;     -   at the final stage the finished anode material is blown through         with pure argon during cooling to 40-60° C. and packaged.

The substantial distinctions of the method being applied for comprise the following:

-   -   the introduction of doping components chromium and vanadium into         the mixture of the initial components results in the         heterovalent substitution of titanium, with the occurrence of         additional free electrons at the d-levels, ensuring the high         electronic conductivity of the anode material;     -   the type of doping elements and their concentrations are         selected in such a way that these elements appear only at the         octahedral positions of the crystal structure, which provides         for cycleability of the material in the electrochemical process;     -   the pulverization of the initial components until particles no         greater than 0.5μ in size are obtained and homogenization of the         mixture promote augmentation of the rate of the basic process:         2Li₂CO₃+(5−2y)TiO₂+y/2Cr₂O₃+y/2V₂O₅→Li₄Ti_(5-2y)(Cr_(y)V_(y))O_(12-x)+2Co₂↑+x/2O₂↑;     -   regulating the volume ratio of the gases in the argon-acetylene         stream from 999:1 to 750:250, respectively, ensures reduction         for obtaining the specified parameter x within the limits from 0         to 0.5 in the finished product;     -   the temperature, rate, and time regimes of the stepwise heat         treatment promotes the running of the basic reaction in the         solid phase without melting, without substantial increase in the         size of the particles of the material, without the formation of         impurity compounds and low-reacting titanium oxide in the form         of rutile, and with achievement of the composition of the         finished product applied for;     -   the final heat treatment stage with pure argon blow-through         prevents the oxidation of the finished anode material during         cooling, while also protecting it against absorption of moisture         from the atmosphere.

The substantial distinctions of the proposed method are necessary and sufficient for the production of anode material for lithium-ion ECCs of the formula being applied for with high electrochemical characteristics:

Electronic conductivity 2 · 10⁻² ohm⁻¹ · cm⁻¹ Electrochemical capacitance 165 ± 5 mA · hour/g Electrochemical potential 1.53 ± 0.01 V

The above and other features of the invention including various novel details of construction and combinations of parts, and other advantages, will now be more particularly described and pointed out in the claims. It will be understood that the particular method and device embodying the invention are shown by way of illustration and not as a limitation of the invention. The principles and features of this invention may be employed in various and numerous embodiments without departing from the scope of the invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

The best embodiment was selected from a large-scale series of trials (more than 100) of production of anode material for lithium-ion ECCs carried out in laboratory conditions of an electrochemical enterprise of the Ural region.

The following commercial chemical reagents were used for the production of the anode material:

-   -   Li2CO3—lithium carbonate;     -   TiO2—titanium oxide (IV), in the form of anatase;     -   Cr2O3—chromium oxide (III);     -   V₂O₅—vanadium oxide (IV);     -   LiOH—lithium hydroxide;     -   Li₂O—lithium oxide;     -   LiNO₃—lithium nitrate;     -   TiO₂ in the form of rutile;     -   TiO₂.xH₂O—titanium hydroxide;     -   (NH₄)₂CrO₃—ammonium chromate;     -   NH₄VO₃—ammonium metavanadate;     -   Li₂CrO₃—lithium chromate;     -   Li₄VO₃—lithium metavanadate.

Example. Production of anode material for lithium-ion ECCs.

For preparation of a mixture of the initial components for the production of anode material for lithium-ion ECCs based on lithium-titanium spinel, TiO₂ (technical grade, anatase, TU [Technical Specifications] 1715-347-00545484-94) and Li₂CO₃ (TU [Technical Specifications] 95.1951-89, LU-1 [lithium carbonate-1] grade) were selected; sources of doping components Cr₂O₃ (GOST [State Standard] 2912-79, OKhP-1 [chromium oxide pigment-1] grade), V₂O₅ (TU [Technical Specifications] 6-09-4093-88, qualification ChDA [analytically pure]) were introduced; wherewith the weighed portions of the initial components for the production of 100 g of finished product with the formula Li₄Ti_(4.95)(CrV)_(0.025)O_(11.9) were, in g:

TiO₂ 86.38163 Li₂CO₃ 32.28549 Cr₂O₃ 0.41506 V₂O₅ 0.49668 Li₄Ti_(4.95)(CrV)_(0.025)O_(11.9) 100 g

It should be noted that the gaseous reaction products were, respectively, in g:

CO₂ 19.22932 O₂ 0.34953

The initial components were homogenized (agitated) and placed in a ball mill for pulverization to particles no greater than 0.5μ in size. The degree of homogeneity of the mixture was characterized by the fact that a random sample of the mixture of reagents weighing no more than 0.1 g contained an excess of no more than 0.1% of any of the components.

The prepared mixture of the components was then placed in a tube furnace with a controlled gaseous atmosphere, creating a volume ratio of the gases in the argon-acetylene stream of 750:250, respectively. The heat treatment was carried out stepwise, according to the following procedure:

-   -   at the first stage the mixture of components was heated to a         temperature of 350° C.;     -   at the second stage the heating was continued in the 350-750° C.         temperature interval at a rate of 10° C./min, which provides for         solid-phase interaction (reduction) of the components in the         main reaction;     -   at the third stage the temperature was increased to 850° C. and         the product obtained were held at this temperature for 1 hour;     -   at the fourth stage the temperature was decreased to 550° C. at         a rate of 4° C./min, and the anode material obtained was held at         this temperature for 2 hours;     -   at the final stage the finished anode material was blown through         with pure argon during cooling to a temperature below 50° C. and         was packaged in containers in an argon atmosphere to prevent         oxidation and absorption of moisture from the atmosphere.

The characteristics of the finished anode material for lithium-ion ECCs are given in the Table; these were determined by means of the following standard analysis methods:

-   -   crystalline structure and phase composition: powder x-ray         diffraction     -   density: gas pycnometry;     -   chemical composition: ISP (inductively coupled plasma         spectroscopy), titrimetric methods;     -   application characteristics: galvanostatic cycling of test         cells, impedance measurements on pressed samples with applied         silver electrodes.

Industrial Applicability

The anode material for lithium-ion ECCs applied for, that possesses high electrochemical capacitance (165±5 mA·hour/g) and electronic conductivity (2.10-2 ohm⁻¹·cm⁻¹), is intended for use in devices operating at high discharge currents, for example, electric transport storage batteries or portable electric power tools. This material can be produced from accessible components on traditional equipment of domestic facilities; this attests to the conformity of the invention to the “industrial applicability” criterion.

While this invention has been particularly shown and described with references to preferred embodiments thereof, it will be understood by those skilled in the art that various changes in form and details may be made therein without departing from the scope of the invention encompassed by the appended claims.

The Characteristics of Anode Materials for Lithium-Ion ECCs

TABLE Anode Material for ECCs No./item Name, Unit of Measurement prototype applied for 1 Chemical formula Li₄Ti₅O_(12-x) Li₄Ti_(5-2y)(Cr_(y) V_(y))O_(12-x) 2 Name lithium-titanium (4:5) oxide 3 Color blue black, blue-black 4 Form powder powder 5 Density, g/cm³ 3.53 ± 0.03 3.57 ± 0.02 6 Decomposition temperature in the 925 925 solid phase, ° C. 7 Melting point, ° C. 1295-1300 1295-1300 8 Crystalline structure cubic, spinel type cubic, spinel type 9 Space group Fd 3m (No. 227) Fd 3m (No. 227) 10 Crystal lattice parameter, Å 8.358 8.368 ± 0.003 11 Electronic conductivity σ_(el) ²⁹⁵, ohm⁻¹ ~10⁻⁵-10⁻⁶ 5 · 10⁻³ cm⁻¹ 12 Electrochemical capacitance, 155-160 165 ± 5 mA · hour/g 13 Electrochemical potential in relation 1.55 1.52 to lithium, V 

1. An anode material for electrochemical cells based on lithium-titanium spinel of a chemical formula, Li₄Ti₅O_(12-x), where x is a deviation from stoichiometry within the limits 0<x<0.02, comprising doping components chromium and vanadium in equivalent quantities to achieve a composition of a formula Li₄Ti_(5-2y)(Cr_(y)V_(y))O_(12-x), where 0.02<x<0.5, and y is a stoichiometric coefficient within the limits 0<y<0.25. 